Product Gallery
Finecast manufactures a wide range of component parts. Here are a few examples.
Drain Trough BiW Casting
Material: Aluminum Alloy A356 Refined Alloy
Mechanical Properties: UTS:180MPa, 0.2 Proof Stress 110Mpa & Elongation 10%
Dimensions: 470mmx513mmx417mm XYZ
Cast Wall Section: 2.5mm consistent complete casting
Cast Weight: 2.8 Kgs
Quantity: 50 pieces
Delivery: MAGMASOFT simulation casting development, Foundry tooling with first produced casting 6 weeks
BiW Casting
Material: Aluminum Alloy A356 Refined Alloy
Mechanical Properties: UTS:180MPa, 0.2 Proof Stress 110Mpa & Elongation 10%
Dimensions: 875mmx466mmx365mm XYZ
Cast Wall Section: 3mm consistent complete casting
Cast Weight: 4.1 Kgs
Quantity: 50 pieces
Delivery: MAGMASOFT simulation casting development, Foundry tooling with first produced casting 6 weeks
Bracket BiW Casting
Material: Aluminium A356 Refined Alloy
Mechanical Properties: UTS:180MPa, 0.2 Proof Stress 110Mpa & Elongation 10%
Dimensions: 479mmx408mmx471mm XYZ
Cast Wall Section: 3mm consistent complete casting
Cast Weight: 2.3 Kgs
Quantity: 50 pieces
Delivery: MAGMASOFT simulation casting development, Foundry tooling with first produced casting 6 weeks
Front BiW Casting
Material: Aluminum Alloy A356 Refined Alloy
Mechanical Properties: UTS:290MPa, 0.2 Proof Stress 210Mpa & Elongation 4%
Dimensions: 855mmx530mmx690mm XYZ
Cast Wall Section: 3.5mm consistent complete casting
Cast Weight: 14 Kgs
Quantity: 50 pieces
Delivery: First delivery finished cast components includes anodise and Ppac nut assembly 14 weeks from bridging sand cast tooling
Chassis BiW Casting
Material: Aluminum Alloy A356 Refined Alloy
Mechanical Properties: UTS:270MPa, 0.2 Proof Stress 210Mpa & Elongation 11%
Dimensions: 1280mmx340mmx680mm XYZ. Internal complete geometry hollow for reduced component weight produced by 3D rapid prototype sand printed high strength internal core
Cast Wall Section: 3mm consistent complete casting
Cast Weight: 19 Kgs
Quantity: 80 pieces
Delivery: First delivery finished cast components includes TiZr coating 12 w14 weeks from bridging sand cast tooling
Shock Tower BiW Casting
Material: Aluminum Alloy BS L99
Mechanical Properties: UTS:230MPa, 0.2 Proof Stress 190Mpa & Elongation 5%
Dimensions: 475mmx430mmx579mm XYZ
Cast Wall Section: 3.5mm consistent complete casting
Cast Weight: 10.1 Kgs
Quantity: 50 pieces
Delivery: MAGMASOFT simulation casting development, Foundry tooling with first produced casting 6 weeks
Central Node BiW Casting
Material: Aluminum Alloy A356 Refined Alloy
Mechanical Properties: UTS:290MPa, 0.2 Proof Stress 210Mpa & Elongation 4%
Dimensions: 1026mmx473mmx362mm XYZ
Cast Wall Section: 4mm consistent complete casting
Cast Weight: 39 Kgs
Quantity: 50 pieces
Delivery: MAGMASOFT simulation casting development, Foundry tooling with first produced casting 6 weeks
Lightweight Battery Casing
Material: Aluminium A356 Refined Alloy
Mechanical Properties: UTS: 260MPa & Elongation = 12%
Dimensions: 580mmx656mmx560mm
Cast Wall Section: 2.5mm consistent complete casting
Quantity: 810 pieces
Delivery: First casting batch 6 weeks including machining and assembly
Engine Block
Material: Aluminium Alloy EN AC-AlSi7Mg0.3
Mechanical Properties: UTS: 180 MPa & Elongation =5%
Dimensions: 430mmx344mmx283mm
Quantity: 230 pieces
Delivery: First batch 6 weeks machined castings from prototype tooling
Main Case Transmission Assembly
Material: Aluminium Alloy A356
Dimensions: 449mmx439mmx443mm
Quantity: 12 pieces
Delivery: Rapid prototype castings from sand printed moulds fully machined in 8 weeks.
Integrated Turbine Manifold
Material: Stainless Austenitic Steel EN1.4849 (GX40NiCrSiNb38-19)
Dimensions: 214mmx163mmx108mm
Wall thickness: 3.5mm to 4 mm complete casting
Quantity: 3 pieces
Delivery: Rapid prototype castings produced from hybrid sand printed synthetic internal core and tooling fully machined in 3.5 weeks
Motorsport Cylinder Head
Material: Aluminium A354
Dimensions: 409mmx246mmx129mm
Weight: 10.3 Kgs
Wall thickness: Nominal wall thickness 3.5mm
Quantity: 50 pieces
Delivery: MAGMASOFT simulation CAST Development, Foundry tooling with first produced casting 6 weeks
Lightweight Shock Tower
Material: Aluminium A356 Refined Alloy
Mechanical Properties: UTS: 189MPa & Elongation =18%
Dimensions: 360mmx310mmx340mm
Cast Wall Section: 2.5mm complete casting
Cast Weight: 3.4 Kgs
Quantity: 120 pieces
Delivery: MAGMASOFT simulation casting development, Foundry tooling with first produced casting 6 weeks
Water Cooled Compressor Housing
Material: Aluminium EN AC-AlSi8Cu3
Dimensions: 266mmx239mmx124mm
Cast Wall Section: 3.5mm complete casting
Cast Weight: 3.2 Kgs
Quantity: 6 pieces
Delivery: Casting from complete rapid prototype printed mould finished machined 4 weeks
Main Frame Antenna
Material: Aluminium Aerospace BS2-169 (A357)
Dimensions: 1415mmx1055mmx965mm
Cast Wall Section: Nominal wall thickness 5mm
Cast Weight: 80 Kgs
Quantity: 12 pieces
Delivery: MAGMASOFT simulation casting development with castings produced from tooling Foundry tooling in 8 weeks
Defence Casting
Material: Aerospace Aluminium BS2 L169
Dimensions: 380mmx192mmx142mm
Cast Wall Section: Nominal wall thickness 3mm
Quantity: Scheduled batches of 50 sets
Summary: Originally designed for the investment casting process, we worked with our Ministry of Defence customer to engineer a sand cast component qualified to Aerospace class 1 standard significantly reducing their programme costs.